Narrow frame touch input sheet, manufacturing method of same, and conductive sheet used in narrow frame touch input sheet

ABSTRACT

A narrow frame touch input sheet, and a conductive sheet used in the narrow frame touch input sheet, are suitable for a capacitive touch sensor having a narrow frame and two layers of transparent conductive film patterns. The conductive sheet includes one or more transparent base sheets stacked into a layer, transparent conductive films, light-excluding conductive electrode films, and first resist layers, which are layered sequentially on the uppermost and lowermost surfaces thereof. The first resist layers are exposed simultaneously on both surfaces, and after development, the transparent and light-excluding conductive electrode films are simultaneously etched, the first resist layers are stripped away, then second resist layers are formed as coating on the both surfaces in an outer edge portion, so that the light-excluding conductive electrode films are etched only in the central window portions. Thus, circuit patterns of the transparent conductive films are exposed.

TECHNICAL FIELD

The present invention relates to a narrow frame touch input sheet, amethod for manufacturing the same, and a conductive sheet used in thenarrow frame touch input sheet, which are suitable for a capacitivetouch sensor having a narrow frame and two layers of transparentconductive film patterns.

BACKGROUND ART

Conventionally, as disclosed in Patent Literature 1, there exists aninvention for forming a touch input device, in which metal films areformed on terminals of the lead line of transparent electrodes, and thena transparent electrode pattern in an input panel area, the metal filmsof the terminals of the lead line, and the transparent electrodes areetched simultaneously.

The invention described in the Patent Literature 1 is concerned with amethod including the following steps as illustrated in FIG. 7. Atransparent electrode made of ITO film 31 is formed on a polyester film30, and a photoresist film 32 is formed and patterned thereon. Next,after covering the photoresist film 32 with a mask 33, a metal film 34made of indium is formed. Then, the mask 33 is removed, and thephotoresist film 32 is stripped using a resist stripping liquid so thatthe metal film 34 is patterned. After that, a second photoresist film 35is formed and patterned on the patterned metal film 34 (see FIG. 7( e)),and the metal film 34 and the ITO film 31 are etched and removedsimultaneously using ferric chloride solution or the like. Finally, thephotoresist film 35 is stripped using the resist stripping liquid.

CITATION LIST Patent Literature

Patent Literature 1: JP-A-5-108264

SUMMARY OF INVENTION Technical Problem

However, the method of Patent Literature 1 has a problem that if theposition of the mask 33 is shifted by even a little, when the secondphotoresist film 35 is formed and patterned on the patterned metal films34 as illustrated in FIG. 7( e), one of metal films 34 becomes thinwhile the other metal film 34 becomes thick so that desired resistanceof the metal film 34 cannot be obtained. Therefore, the method cannot beapplied to a narrow frame touch input sheet in which the metal film 34is thin and is required to have a resistance within a predeterminedrange.

In addition, as to a capacitive touch input sheet, it is usuallynecessary to stack a transparent conductive film pattern formed in the Xdirection and a transparent conductive film pattern formed in the Ydirection via an insulation layer between them. Because the metal filmand the transparent electrode cannot be formed in alignment on bothsurfaces with each other by the method described in Patent Literature 1,there is a problem that it is necessary to manufacture two touch inputsheets and to glue them together in alignment. As a result, there isalso a problem that the productivity is lowered and that transmittanceof a transparent window portion is decreased or thickness thereof isincreased.

Therefore, an object of the present invention is to solve theabove-mentioned problem and to provide a narrow frame touch input sheet,a method for manufacturing the same, and a conductive sheet used in thenarrow frame touch input sheet, which are suitable for a capacitivetouch sensor having a narrow frame and two layers of transparentconductive film patterns.

Solution to Problem

According to a first aspect of the present invention, a narrow frametouch input sheet is provided, which includes one or more transparentbase sheets stacked into a layer, transparent conductive films formed ona front surface and a rear surface of the one transparent base sheet oron uppermost and lowermost surfaces of the stacked transparent basesheets, a light-excluding conductive electrode film formed on each ofthe transparent conductive films, and a first resist layer formed oneach of the light-excluding conductive electrode films. The transparentconductive films and the light-excluding conductive electrode films in acentral window portion of the one or more the base sheets are formed indesired patterns stacked without misalignment through etching afterexposure and development of the first resist layer. The transparentconductive films and the light-excluding conductive electrode films inan outer edge portion of the one or more base sheets are formed in afine wiring circuit pattern stacked without misalignment through etchingafter exposure and development of the first resist layers. A circuitpattern is constituted of the transparent conductive films in thecentral window portion through removing the first resist layers, andfurther etching and removing the light-excluding conductive electrodefilms in the central window portion.

According to a second aspect of the present invention, the narrow frametouch input sheet of the first aspect is provided, which furtherincludes second resist layers each of which covers the transparentconductive film and the light-excluding conductive electrode film in theouter edge portion.

According to a third aspect of the present invention, the narrow frametouch input sheet of the first aspect or the second aspect is provided,in which the one or more base sheets are plastic films.

According to a fourth aspect of the present invention, the narrow frametouch input sheet of any one of the first to third aspects is provided,in which the light-excluding conductive electrode film is a copper foilhaving a thickness of 20 to 1000 nm.

According to a fifth aspect of the present invention, the narrow frametouch input sheet of any one of the first to fourth aspects is provided,which is a capacitive type.

According to a sixth aspect of the present invention, the narrow frametouch input sheet of any one of the first to fifth aspects is provided,which further includes transparent protection films adhered to bothsurfaces of the structure.

According to a seventh aspect of the present invention, the narrow frametouch input sheet of the sixth aspects is provided, in which thetransparent protection films are composed of cyclic olefin resin films.

According to an eighth aspect of the present invention, the narrow frametouch input sheet of any one of the first to seventh aspects isprovided, in which a retardation value in the central window portion is20 nm or smaller.

According to a ninth aspect of the present invention, a conductive sheetis provided, which includes one or more transparent base sheets stackedinto a layer, transparent conductive films formed on a front surface anda rear surface of the one transparent base sheet or on uppermost andlowermost surfaces of the stacked transparent base sheets, alight-excluding conductive electrode film formed on each of thetransparent conductive films, and a first resist layer formed on each ofthe light-excluding conductive electrode films.

According to a tenth aspect of the present invention, the conductivesheet of the ninth aspect is provided, in which the one or more basesheets are plastic films.

According to an eleventh aspect of the present invention, the conductivesheet of the ninth aspect or the tenth aspect is provided, in which thelight-excluding conductive electrode film is a copper foil having athickness of 20 to 1000 nm.

According to a twelfth aspect of the present invention, a method formanufacturing a narrow frame touch input sheet is provided, whichincludes forming and stacking transparent conductive films,light-excluding conductive electrode films, and first resist layerssequentially on both surfaces of a transparent base sheet; exposing anddeveloping the first resist layers simultaneously on the both surfaces;etching the transparent conductive films and the light-excludingconductive electrode films simultaneously on the both surfaces;stripping the first resist layers so as to form a fine wiring circuitpattern with the stacked transparent conductive film and light-excludingconductive electrode film in an outer edge portion on each of the twosurfaces of the stacked base sheets; forming a second resist layer tocover the fine wiring circuit pattern on each surface of the base sheet;and etching only the light-excluding conductive electrode film layer onwhich the second resist layer is not formed, so that a circuit patternof the transparent conductive film is exposed in a central windowportion on each surface of the base sheet.

According to a thirteenth aspect of the present invention, a method formanufacturing a narrow frame touch input sheet is provided, whichincludes forming and stacking a transparent conductive film, alight-excluding conductive electrode film, and a first resist layersequentially on each of two transparent base sheets; stacking the basesheets to be opposite to each other so that the transparent conductivefilms, the light-excluding conductive electrode films, and the firstresist layers are formed on both surfaces of the stacked base sheets;exposing and developing the first resist layers simultaneously on theboth surfaces; etching the transparent conductive films and thelight-excluding conductive electrode films simultaneously on the bothsurfaces; stripping the first resist layers so as to form a fine wiringcircuit pattern with the sequentially stacked transparent conductivefilm and light-excluding conductive electrode film in an outer edgeportion on each of the two surfaces of the stacked base sheets; forminga second resist layer to cover the fine wiring circuit pattern on eachsurface of the stacked base sheets; and etching only the light-excludingconductive electrode film layer in a central window portion on which thesecond resist layer is not formed on each surface of the stacked basesheets so that a circuit pattern of the transparent conductive film isexposed.

Advantageous Effects of Invention

The narrow frame touch input sheet and the manufacturing method thereofaccording to the present invention are characterized in that thetransparent conductive film of the conductive sheet and thelight-excluding conductive electrode film are etched simultaneously, andthe fine wiring circuit pattern is formed in the outer edge portion inwhich the transparent conductive film and the light-excluding conductiveelectrode film are stacked sequentially with the same pattern withoutmisalignment. After that, the second resist layer is formed to cover thefine wiring circuit pattern, and only the light-excluding conductiveelectrode film layer on which the second resist layer is not formed isetched so that the circuit pattern of the transparent conductive film isexposed in the central window portion.

Therefore, a delicate and fine wiring circuit pattern can be formed, andthat the touch input sheet having a very narrow frame can bemanufactured.

In addition, the step of forming the second resist layer that requiresalignment can be performed with alignment accuracy such that the finewiring circuit pattern in the outer edge portion can be covered.Therefore, the narrow frame touch input sheet can be obtained with highproductivity.

In addition, the narrow frame touch input sheet and the manufacturingmethod thereof according to the present invention are characterized inthat the circuit pattern and the fine wiring circuit pattern of thetransparent conductive film are formed on both surfaces of the basesheet. Further, the narrow frame touch input sheet of the presentinvention is characterized in being a capacitive type. Therefore, thecapacitive narrow frame touch input sheet can be manufactured, in whichthe circuit pattern and the fine wiring circuit pattern of the XYtransparent conductive films are formed using only one base sheet as acore.

In addition, because the structure can be composed of only one basesheet as a core, the capacitive type narrow frame touch input sheet witha high transparency and small thickness can be manufactured.

In addition, the narrow frame touch input sheet and the conductive sheetof the present invention are characterized in that the light-excludingconductive electrode film layer is constituted of a copper foil having athickness of 20 to 1000 nm. Therefore, because of the good electricalconductivity of the conductive electrode film layer, the narrow frametouch input sheet having good responsiveness can be manufacturedefficiently.

In addition, because of the high light-excluding property of theconductive film layer for an electrode, when the first resist layers onboth surfaces are patterned simultaneously through exposing and thelike, the exposing light beam can be effectively prevented from reachingthe first resist layer on the opposite surface. Therefore, the narrowframe touch input sheet having the circuit patterns and the fine wiringcircuit patterns formed on both surfaces of the base sheet can bemanufactured with high productivity and high quality.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a schematic cross sectional view illustrating an example of anarrow frame touch input sheet according to the present invention, inwhich circuit patterns and fine wiring circuit patterns are formed onfront and rear surfaces of a single transparent base sheet.

FIG. 2( a) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 2( b) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 2( c) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 2( d) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 2( e) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 2( f) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 3 is a schematic cross sectional view illustrating an example of anarrow frame touch input sheet according to the present invention, inwhich circuit patterns and fine wiring circuit patterns are formed onuppermost and lowermost surfaces of two layers of stacked transparentbase sheets.

FIG. 4( a) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 4( b) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 4( c) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 4( d) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 4( e) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 4( f) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 4( g) is a schematic diagram illustrating a step of manufacturingthe narrow frame touch input sheet.

FIG. 5 is a schematic cross sectional view illustrating an example inwhich protection films are adhered to the narrow frame touch input sheetillustrated in FIG. 1.

FIG. 6 is a schematic cross sectional view illustrating an example inwhich protection films are adhered to the narrow frame touch input sheetillustrated in FIG. 2( e).

FIG. 7 is a diagram illustrating an electrode forming step of the touchinput device described in Patent Literature 1.

FIG. 8 is a plan view illustrating an example of shape and arrangementof the circuit pattern formed in a central window portion of the narrowframe touch input sheet.

DESCRIPTION OF EMBODIMENTS

Hereinafter, best embodiments of the present invention will be describedwith reference to the drawings.

First Embodiment

Hereinafter, the present invention will be described in detail withreference to the drawings. FIG. 1 is a schematic cross sectional viewillustrating an example of a narrow frame touch input sheet as acapacitive touch sensor according to the present invention, in whichcircuit patterns and fine wiring circuit patterns are formed on bothsurfaces, i.e. on front and rear surfaces, of a single transparent basesheet. FIGS. 2( a) to 2(f) are schematic cross sectional viewsillustrating steps of manufacturing the capacitive touch sensor. In thefigures, reference numeral 1 denotes a light-excluding conductiveelectrode film layer, reference numeral 3 denotes a transparentconductive film, reference numeral 5 denotes a narrow frame touch inputsheet, reference numeral 7 denotes a base sheet, reference numeral 10denotes a fine wiring circuit pattern, numeral 12 denotes a mask,reference numeral 14 denotes an exposing light beam, reference numeral16 denotes a first resist layer, reference numeral 18 denotes a secondresist layer, reference numeral 20 denotes a capacitive touch sensor,reference numeral 22 denotes an outer edge portion of the narrow frametouch input sheet 5, reference numeral 24 denotes a central windowportion of the narrow frame touch input sheet 5, and reference numeral28 denotes an external circuit.

The narrow frame touch input sheet 5 of the present invention has thefollowing structure. In the central window portion 24 on the base sheet7, a circuit pattern of a transparent conductive film 3 is formed. Inthe outer edge portion 22, a fine wiring circuit pattern 10 is formed inwhich the transparent conductive film 3 and a light-excluding conductiveelectrode film 1 are stacked sequentially. The narrow frame touch inputsheet 5 has a feature that the transparent conductive film 3 and thelight-excluding conductive electrode film 1 of the fine wiring circuitpattern 10 are formed and stacked in the same pattern withoutmisalignment. Further, the circuit pattern and the fine wiring circuitpattern 10 of the transparent conductive film 3 can be formed on bothsurfaces of a single transparent base sheet (see FIG. 1).

A method for manufacturing the above-mentioned narrow frame touch inputsheet 5, in which the circuit pattern and the fine wiring circuitpattern 10 of the transparent conductive film 3 are formed on bothsurfaces of a single transparent base sheet, includes the followingsteps. First, the transparent conductive films 3, the light-excludingconductive electrode films 1, and first resist layers 16 are formedsequentially along the entire surface of both front and rear surfaces ofa single transparent base sheet 7, so that a conductive sheet (see FIG.2( a)) is obtained. After that, masks 12 of desired patterns are placedon both the front and rear surfaces, and the first resist layers 16 arepatterned by exposing and developing (see FIG. 2( b)). In this case, thelight-excluding conductive electrode film 1 on one side blocks anexposing light beam 14 from the other side. Therefore, when bothsurfaces are exposed simultaneously using different mask patterns, thepattern of the first resist layer 16 on one side has no influence on thepattern of the first resist layer 16 on the opposite side. Therefore,because both surfaces can be exposed simultaneously, alignment betweenthe first resist layers 16 on the front and rear surfaces can beperformed easily, and both surfaces can be patterned in a single step sothat productivity can be improved.

Note that the alignment between a front mask and a rear mask can beperformed using a known mask alignment method for a double-sidedexposure apparatus. For instance, mask alignment marks are formed oneach of the front mask and the rear mask, and an optical read sensorsuch as a camera reads a superposed state of a pair of mask alignmentmarks, so that relative positional information between the front maskand the rear mask can be obtained. Then, based on the obtainedpositional information, a mask position adjustment mechanism moves thefront mask and the rear mask relatively to each other so that centers ofthe mask alignment marks are overlapped with each other, therebyaligning the front mask and the rear mask with each other.

Next, the transparent conductive film 3 and the light-excludingconductive electrode film 1 are simultaneously etched using etchingliquid such as ferric chloride, so that a thin line pattern is formed(see FIG. 2( c)). Next, the first resist layer 16 is stripped using theresist stripping liquid so that the light-excluding conductive electrodefilm 1 is exposed. After that, a second resist layer 18 is formed onlyon the exposed light-excluding conductive electrode film 1 along theouter edge portion 22 (see FIG. 2( d)). It is sufficient as long as thesecond resist layer 18 covers the light-excluding conductive electrodefilm 1 of the outer edge portion 22 along with the transparentconductive film 3. Therefore, the second resist layer 18 is not requiredto be aligned so precisely. For this reason, there is little defect whenthe second resist layer 18 is formed, and productivity is improved.

Next, etching is performed using a special etching liquid such asacidified hydrogen peroxide. Then, the outer edge portion 22, on whichthe second resist layer 18 is formed, remains as is, while thelight-excluding conductive electrode film 1 in the central windowportion 24, in which the second resist layer 18 is not formed and thelight-excluding conductive electrode film 1 is exposed, is removed bythe etching so that the transparent conductive film 3 thereunder isexposed (see FIG. 2( e)). The central window portion 24 becomes adisplay portion in which transparent conductive films are formed on bothsurfaces, while the light-excluding conductive electrode film 1 formedin the outer edge portion 22 and the transparent conductive film 3formed thereunder with the same pattern become the fine wiring circuitpattern 10. Note that if the transparent conductive film 3 is made of anamorphous material, it is preferred to have the material crystallized bymeans of heat treatment before the etching. It is becausecrystallization improves etching resistance, so that only thelight-excluding conductive electrode film 1 can selectively be etchedmore easily.

The end portion of the fine wiring circuit pattern 10 formed on bothsurfaces of the narrow frame touch input sheet 5 by the method describedabove is connected to an external circuit 28 that includes IC chips, andthus the capacitive touch sensor 20 having the transparent conductivefilms 3 formed on both surfaces of the base sheet 7 is manufactured (seeFIG. 2( f)).

Here, the circuit pattern formed in the central window portion 24 of thecapacitive touch sensor 20 will be additionally described. In theschematic cross sectional view of the narrow frame touch input sheet 5attached to this specification, the circuit pattern has been simplified.In actual practice, the circuit pattern is different between the frontand rear surfaces. For instance, as illustrated in FIG. 8, the rear sideof the base sheet 7 is provided with a plurality of rhombus electrodes46 having a rhombic shape in plan view and a connection wiring 469 thatpasses through the rhombus electrodes 46 in the vertical direction (Ydirection) in the figure. The plurality of rhombus electrodes 46 and theconnection wiring 469 are electrically connected to each other. Inaddition, sets of the connection wiring 469 and the plurality of rhombuselectrodes 46 are arranged in a repeating pattern in the lateraldirection (X direction) in the figure. On the other hand, in the samemanner, the front side of the base sheet 7 is provided with a pluralityof rhombus electrodes 47 and a connection wiring 479 that passes throughthe rhombus electrodes 47. However, in this case, the extendingdirection of the connection wiring 479 is different from that of theconnection wiring 469 and is the lateral direction (X direction) in thefigure. In addition, sets of the connection wiring 479 and the pluralityof rhombus electrodes 47 are arranged in a repeating pattern in thevertical direction (Y direction) in the figure. Further, as can beunderstood from FIG. 8, the rhombus electrodes 46 are arranged to fillgaps formed between the connection wirings 479, while the rhombuselectrodes 47 are arranged to fill gaps formed between the connectionwirings 469. Further as illustrated in FIG. 8, the rhombus electrodes 46and the rhombus electrode 47 are arranged complementarily. In otherwords, the rhombus electrodes 47 are arranged so as to fill rhombic gapsthat are formed as a result of the rhombus electrodes 46 being arrangedas a matrix. As described above, according to the present invention, thelight-excluding conductive electrode film 1 on one side blocks theexposing light beam 14 from the other side. Therefore, when bothsurfaces are exposed simultaneously, the pattern of the first resistlayer 16 on one side has no influence on the pattern of the first resistlayer 16 on the opposite side. Thus, different circuit patterns can beformed on the front and rear surfaces.

Because the X direction electrodes and the Y direction electrodes arearranged so as to form a lattice, if a finger or the like of a usertouches any position on the lattice (for example, a position indicatedby the broken line circle FR), a capacitor is formed between the fingeror the like and the X direction electrode in contact. In addition, acapacitor is formed between the finger or the like and the Y directionelectrode in contact. The formation of the capacitors increases thecapacitances of the X direction electrode and the Y direction electrode.A position detection unit of the external circuit 28 detects a variationof the capacitance generated in this case, and further detects the Xdirection electrode and the Y direction electrode having the maximumcapacitance, so that a set of X coordinate and Y coordinate can beobtained as specific values indicating the position that is touched inthe central window portion 24.

Next, individual layers constituting the above-mentioned narrow frametouch input sheet 5 will be described in detail.

First, the base sheet 7 is made of a transparent sheet having athickness of approximately 30 to 2000 μm, and the material thereof is aplastic film such as polyester resin, polystyrene resin, olefin resin,polybutylene terephthalate resin, polycarbonate resin, acrylic resin, orthe like, or a glass material.

Here, when the base sheet 7 of the conductive sheet is a plastic film, aproblem of film elongation may occur. For this reason, it is preferredto pattern the first resist layers 16 on both surfaces of the conductivesheet by simultaneous exposure of both surfaces. It is because, if thepatterning of the first resist layers 16 is preformed by exposing onesurface at a time, the following problem will occur. When the patterningof one side is finished and the conductive sheet is turned over to beset into the exposing device again, if the base sheet 7 is elongated, amisalignment occurs between the circuit patterns on the front surfaceand the rear surface. In the example illustrated in FIG. 8, because therhombus electrodes 46 and the rhombus electrodes 47 are arranged in acomplementary relationship, if a misalignment occurs between the circuitpatterns on the front surface and the rear surface, the correct functionof the capacitive touch sensor 20 cannot be achieved.

As the light-excluding conductive electrode film layer 1, a single metalfilm having high electrical conductivity and good light-excludingproperty may be used or a layer made of an alloy or compound of themetal maybe used. The light-excluding conductive electrode film layer 1can be formed by a vacuum deposition method, a sputtering method, an ionplating method, a plating method, or the like. Further, it is importantthat there is an etchant that does not etch the transparent conductivefilm but etches the conductive electrode film layer itself. As apreferred example of the metal, aluminum, nickel, copper, silver, andthe like may be used. In particular, a metal film made of copper foilhaving a thickness of 20 to 1000 nm is preferable in terms of electricalconductivity and light-excluding property, and can be easily etched byhydrogen peroxide solution in acid atmosphere, which does not etch thetransparent conductive film. In addition, such a metal film is alsopreferred because it can be easily connected to the external circuit.Preferably, the thickness of the metal film is 30 nm or larger. Morepreferably, the thickness is 100 to 500 nm. It is because thelight-excluding metal film layer 1 having a high electrical conductivitycan be obtained by setting the thickness thereof to 100 nm or larger,and the light-excluding metal film layer 1 that can be easily handledand is superior in terms of processability can be obtained by settingthe thickness thereof to 500 nm or smaller.

As the transparent conductive film 3, a layer made of a metal oxide suchas indium tin oxide or zinc oxide may be used, and the transparentconductive film 3 can be formed by a vacuum deposition method, asputtering method, an ion plating method, a plating method, or the like.The thickness thereof ranges from approximately tens to a few hundredsnanometers. It is necessary that the transparent conductive film 3 canbe easily etched together with the light-excluding conductive electrodefilm 1 using a solution of ferric chloride or the like, but cannot beeasily etched using the etching liquid for the light-excludingconductive electrode film layer 1 such as the hydrogen peroxide solutionin acid atmosphere. Further, it is preferable for the transparentconductive film 3 to have a light transmittance of 80% or higher and asurface resistance of a few milliohms to a few hundred milliohms. Inaddition, it is possible to use a conductive polymer film such asthiophene or a conductive fiber film including metal nanowires or carbonnanotubes for the transparent conductive film 3. In this case, thetransparent conductive film 3 can be formed by a printing method or anapplying method.

It is preferable that the first resist layer 16 is made of a photoresistmaterial such as tetramethylammonium hydroxide that can be exposed by alaser beam or a metal halide lamp and can be developed by an alkalinesolution or the like. It is because the exposure and development usingthe photoresist material can securely form the fine wiring circuitpattern 10 having small width, so that the narrow frame touch inputsheet 5 having a narrower frame can be manufactured. In addition,according to the present invention, since the light-excluding conductiveelectrode film layer 1 is formed as described above, if the first resistlayer 16 is made of a photoresist material, the exposure and developmentcan be performed simultaneously on the front surface and on the rearsurface, so that the narrow frame touch input sheet 5 can bemanufactured with a very high productivity. The first resist layer 16can be formed through a general-purpose printing method such as gravure,screen, offset, or the like, or a method using any coater, an applyingmethod, or a dipping method.

Material of the second resist layer 18 is not limited to a specific oneas long as it is resistant to the etching liquid for the light-excludingconductive electrode film layer 1 such as hydrogen peroxide solution inacid atmosphere. In addition, the second resist layer 18 may remainpermanently as a protection film except for the portion that serves asconnection terminals with the external circuit 28. Therefore, unlike thefirst resist layer 16, the second resist layer 18 does not always haveto be removed through development. Note that FIG. 1 illustrates the casewhere the second resist layer 18 is removed. As the material that mayserve as a protection film, a thermosetting resin such as epoxy,urethane, or acrylic may be used, or an ultraviolet curing resin such asurethane acrylate or cyanoacrylate may be used. The same method forforming the first resist layer 16 can be adopted to form the secondresist layer 18.

In addition, on this second resist layer 18, a design pattern layer maybe formed so as to hide the fine wiring circuit pattern 10 and toimprove exterior design. The design pattern layer may be formed by usingpolyvinyl, polyamide, polyacryl, polyurethane, or alkyd resin as abinder and using color ink containing appropriate color pigment or dyeas a coloring agent. In addition, it is possible to use pearl pigmentcontaining a coloring agent made of metal particles such as aluminum,titanium, or bronze, or mica on which titanium oxide is coated. Thedesign pattern layer can be formed through a general-purpose printingmethod such as gravure, screen, or offset, any coating method, or anapplying method.

Second Embodiment

In the example of the narrow frame touch input sheet described above,the circuit patterns and fine wiring circuit patterns are formed on thefront and rear surfaces of the single transparent base sheet. However,the present invention is not limited to this structure.

For instance, the circuit pattern and the fine wiring circuit pattern 10of the transparent conductive film 3 may be formed on the uppermost andlowermost surfaces of a plurality of transparent base sheets 7 that arestacked together (see FIG. 3). In order to obtain such a narrow frametouch input sheet, firstly, two base sheets 7 having a small thicknessare used, and the transparent conductive film 3, the light-excludingconductive electrode film 1, and the first resist layer 16 aresequentially formed along the entire surface of one side of each of thebase sheets 7. After that, the two base sheets 7 are stacked to beopposite to each other, so that the conductive sheet (see FIG. 4( a)) isobtained. As a method of stacking the base sheets 7, a heat laminatemethod and a dry laminate method using an adhesive layer may be used.When the base sheets 7 are stacked using the adhesive layer, it ispossible to adjust the total thickness of the stacked body with theadhesive layer having a core.

Next, masks 12 having desired patterns are placed on the uppermost andlowermost surfaces of the two stacked transparent base sheets, and thefirst resist layers 16 are patterned through exposure and development(see FIG. 4( b)).

Next, the transparent conductive film 3 and the light-excludingconductive electrode film 1 are etched simultaneously using an etchingliquid such as ferric chloride so as to form a thin line pattern (seeFIG. 4( c)). Next, the first resist layer 16 is stripped using theresist stripping liquid so that the light-excluding conductive electrodefilm 1 is exposed (see FIG. 4( d)). After that, a second resist layer 18is formed only on the exposed light-excluding conductive electrode film1 along the outer edge portion 22 (see FIG. 4( e)).

Next, etching is performed using a special etching liquid such asacidified hydrogen peroxide. Then, the outer edge portion 22, on whichthe second resist layer 18 is formed, remains as is, while thelight-excluding conductive electrode film 1 in the central windowportion 24, in which the second resist layer 18 is not formed and thelight-excluding conductive electrode film 1 is exposed, is removed bythe etching, so that the transparent conductive film 3 thereunder isexposed (see FIG. 4( f)). The central window portion 24 becomes adisplay portion in which transparent conductive films are formed on bothsurfaces, while the light-excluding conductive electrode film 1 formedin the outer edge portion 22 and the transparent conductive film 3formed thereunder with the same pattern become the fine wiring circuitpattern 10. Note that FIG. 3 illustrates the case where the secondresist layer 18 is removed after the etching.

The end portion of the fine wiring circuit pattern 10 formed on bothsurfaces of the narrow frame touch input sheet 5 obtained by the methoddescribed above is connected to an external circuit 28 that includes ICchips. Thus, the capacitive touch sensor 20 having the transparentconductive films 3 formed on both surfaces of the two stacked basesheets 7 is manufactured (see FIG. 4 (g)).

<Variations>

In order to etch the above-mentioned transparent conductive film 3 andthe light-excluding conductive electrode film 1 simultaneously andefficiently, it is necessary to use the ferric chloride solution havinga fairly high concentration. If the cleansing with water is insufficientafter the etching, there is a problem that the transparent conductivefilm 3 or the light-excluding conductive electrode film 1 would beeroded so that the electrical characteristic would be deteriorated whentested in an environment of high temperature and high humidity.Therefore, it is necessary to prevent the erosion in an application inwhich the wiring circuit is made of thin lines while low resistance mustbe maintained for a long term, and the transparent electrode is alsorequired to be in a predetermined resistance range for a long term, likethe narrow frame touch input sheet.

As a measure against the erosion, it is preferred that the narrow frametouch input sheet of the present invention is further provided withtransparent protection films adhered to both surfaces of theabove-mentioned structure (see FIG. 5). It is preferred that thetransparent protection film 30 is good in terms of moisture resistanceand is made of a film having optical isotropy such that a retardationvalue in the central window portion of the narrow frame touch inputsheet can be 20 nm or smaller. It is because, if the retardation valueis a large value above 20 nm, emitting light and transmitting light fromthe touch input sheet would split into two light waves havingoscillation directions perpendicular to each other, and a phase shift ofthe light wave would be generated so that the color of the emittinglight from the touch input sheet would be changed, or that color shadingmay occur.

As a material suitable for the transparent protection film 30, cyclicolefin resin, polyethersulphon resin, polyarylate resin, amorphouspolyolefin resin, and the like may be used. Among them, the cyclicolefin resin has a high glass transition temperature and a lowphotoelastic coefficient so that it is optimal as a material in which astable retardation value can be obtained.

The thickness of the transparent protection film 30 may be selectedappropriately within the range of 10 to 500 μm. If the thickness issmaller than 10 μm, it becomes difficult for the film to serve as theprotection film for improving the resistance. If the thickness is largerthan 500 μm, it becomes difficult to set the retardation value in thecentral window portion to 20 nm or smaller.

The method of adhering the transparent protection film 30 is not limitedto the heat laminate method or the lamination with adhesive. Inaddition, it is possible to adhere the transparent protection films 30having different material or thickness to the light-excluding electrodeconductive film layer 1 and the transparent conductive film 3,respectively.

Note that the retardation (birefringence) means a phenomenon in whichthe light entering a crystal or other anisotropic substance is splitinto two light waves having oscillation directions that are orthogonalto each other. When non-polarized light enters a material havingbirefringence, the incident light is split into two, which haveoscillation directions that are orthogonal to each other. One of them isreferred to as vertically polarized light, and the other is referred toas horizontally polarized light. The vertically polarized light becomesan extraordinary ray, while the horizontally polarized light becomes anordinary ray. The ordinary ray has a propagation rate that does notdepend on a propagation direction. The extraordinary ray has apropagation rate that varies depending on the propagation direction. Thebirefringence material has a direction in which the two rays have thesame rate, and the direction is referred to as an optical axis. Theretardation value Δnd is expressed by Δnd=(nx−ny)d. Here, d denotes thethickness of a test sample, and nx and ny denote refractive indexes ofthe test sample.

Note that also in the case where the second resist layer 18 is notstripped, the second resist layer 18 is deteriorated or swelled slightlyby the special etching liquid, so that it is insufficient to protect thetransparent conductive film 3 and the light-excluding conductiveelectrode film 1 for a long term. Therefore, the transparent protectionfilm 30 covers not only the exposed transparent conductive film 3 butalso the light-excluding conductive electrode film 1 so that furtherprotection can be achieved (see FIG. 6).

EXAMPLE 1

(1) Manufacturing of the Narrow Frame Touch Input Sheet

As the base sheet, a colorless and transparent soda glass plate having athickness of 1 mm was used. On the front and rear surfaces of the basesheet, the transparent conductive films made of indium tin oxide wereformed through sputtering method to have a thickness of 200 nm. On them,copper films were formed as the light-excluding conductive electrodefilms through sputtering method to have a thickness of 500 nm. On them,tetramethylammoniumhydrooxide layers were formed as the first resistlayers through spin coating. The mask having an X direction electrodepattern was placed on the front side, while the mask having a Ydirection electrode pattern was placed on the rear side. Then, the frontand rear surfaces were exposed simultaneously using a metal halide lamp,and were developed in alkali solution.

Next, the indium tin oxide film and the copper film were etchedsimultaneously using ferric chloride etching liquid. Then, in thecentral window portion, the X direction electrode pattern was exposed onthe front side, while the Y direction electrode pattern was exposed onthe rear side. In the outer edge portion surrounding the central windowportion, thin wiring patterns having an average line width of 20 μm wereexposed on the front and rear surfaces. Next, thermosetting acrylicresin layers were formed as the second resist layers to cover the thinwiring patterns through screen printing to have a thickness of 10 nm.Next, dipping in the hydrogen peroxide solution in acid atmosphere, theexposed copper film in the exposed central window portion was etched andremoved, so that only the indium tin oxide film formed thereunderremained.

(2) Manufacturing and Evaluation of the Capacitive Touch Sensor

By the method described above, the narrow frame touch input sheet havingthe following structure was obtained. Only the indium tin oxide films ofthe X direction electrode pattern and the Y direction electrode patternare formed in the central window portion, on both surfaces of the basesheet. In the outer edge portion of each side, the fine wiring circuitis formed in which the copper film having the same pattern is formed onthe indium tin oxide film, which is covered with the thermosettingacrylic resin layer. The end portion of the fine wiring circuit patternformed on the narrow frame touch input sheet was connected to theexternal circuit that includes IC chips, so as to evaluate theperformance as the capacitive touch sensor. A good result was obtained.In addition, light transmittance in the central window portion wasmeasured, and a good value of 90% was obtained.

EXAMPLE 2

Two colorless polyester films having a thickness of 200 μm were used asthe base sheets. On one surface of each base sheet, the transparentconductive film, the light-excluding conductive electrode film, thefirst resist layer, and the second resist layer were formedsequentially. The base sheets were stacked so as to be opposite to eachother, so that the transparent conductive film, the light-excludingconductive electrode film, and the first resist layer were formed onboth surfaces of the stacked base sheets. After that, the X directionelectrode pattern was formed on the front surface in the central windowportion, and the Y direction electrode pattern was formed on the rearsurface in the central window portion. Other than that, the same methodas in Example 1 was used, and the narrow frame touch input sheet wasobtained. The end portion of the fine wiring circuit pattern formed onthe narrow frame touch input sheet was connected to the external circuitthat includes IC chips, so as to evaluate the performance as thecapacitive touch sensor. A good result was obtained similarly to Example1.

EXAMPLE 3

A colorless and transparent polyester film having a thickness of 100 μmwas used as the base sheet. On the front and rear surfaces of the basesheet, the transparent conductive film made of indium tin oxide having athickness of 200 nm was formed through sputtering method. On thetransparent conductive film, a copper film was formed as thelight-excluding conductive electrode film through sputtering method tohave a thickness of 300 nm. On the copper film, the first resist layermade of novolac resin was formed through gravure coating. The maskhaving the X direction electrode pattern was placed on the front side,while the mask having the Y direction electrode pattern was placed onthe rear side. The front and rear surfaces were exposed simultaneouslyusing a metal halide lamp, and were developed in alkali solution.

Next, the indium tin oxide film and the copper film were etchedsimultaneously using the ferric chloride etching liquid. Then, in thecentral window portion, the X direction electrode pattern was exposed onthe front side, while the Y direction electrode pattern was exposed onthe rear side. In the outer edge portion surrounding the central windowportion, thin wiring patterns having an average line width of 20 μm wereexposed on the front and rear surfaces. Next, a thermosetting acrylicresin layer were formed as the second resist layer to cover the thinwiring patterns through screen printing to have a thickness of 10 μm.Next, dipping in the hydrogen peroxide solution in acid atmosphere, theexposed copper film in the exposed central window portion was etched andremoved, so that only the indium tin oxide film formed thereunderremained.

Next, the transparent protection films made of cyclic olefin resinhaving a thickness of 50 μm were adhered to both surfaces with acrylicadhesive, so as to cover the transparent electrode pattern in thecentral window portion and the thermosetting acrylic resin layer in theouter edge portion on each side. By the method described above, thenarrow frame touch input sheet having the following structure wasobtained. Only the indium tin oxide films of the X direction electrodepattern and the Y direction electrode pattern are formed in the centralwindow portion, on both surfaces of the base sheet. In the outer edgeportion of each side, the fine wiring circuit is formed in which thecopper film having the same pattern is formed on the indium tin oxidefilm, which is covered with the thermosetting acrylic resin layer. Thetransparent electrode pattern and the thermosetting acrylic resin layeron each side are covered with the transparent protection film.

The end portion of the fine wiring circuit pattern formed on theobtained narrow frame touch input sheet was connected to the externalcircuit that includes IC chips, so as to evaluate the performance as thecapacitive touch sensor for long term. A result was obtained indicatingthat a stable electrical characteristic can be maintained. In addition,a retardation value in the central window portion was measured, and wasfound to be 20 nm. Problems such as color shading did not occur.

EXAMPLE 4

Two colorless and transparent polyester films having a thickness of 38μm were used as the base sheets. On one surface of each base sheet, thetransparent conductive film, the light-excluding conductive electrodefilm, the first resist layer, and the second resist layer were formedsequentially. The base sheets were stacked so as to be opposite to eachother so that the transparent conductive film, the light-excludingconductive electrode film, and the first resist layer were formed onboth surfaces of the stacked base sheets. Then, the X directionelectrode pattern was formed on the front surface in the central windowportion, and the Y direction electrode pattern was formed on the rearsurface in the central window portion. After that, the transparentprotection film made of cyclic olefin resin having a thickness of 30 μmis adhered only to the electrode pattern on the surface in the centralwindow portion of each side. Other than that, the same method as inExample 3 was used, and the narrow frame touch input sheet was obtained.The end portion of the fine wiring circuit pattern formed on the narrowframe touch input sheet was connected to the external circuit thatincludes IC chips, so as to evaluate the performance as the capacitivetouch sensor for a long term. A result was obtained indicating that astable electrical characteristic can be maintained. In addition, aretardation value in the central window portion was measured, and wasfound to be 10 nm. Problems such as color shading did not occur.

The present invention has been fully described with reference to theattached drawings related to the preferred embodiments, but variousvariations and modifications thereof would be apparent for a skilledperson in the art. It should be understood that such variations andmodifications are included in the scope of the present invention asdefined by the attached claims unless they deviate from the scope.

INDUSTRIAL APPLICABILITY

The present invention may be used in the narrow frame touch input sheetthat can be applied to an input device of a cellular phone, a PDA, or asmall PC, which has a display screen such as a liquid crystal panel.

REFERENCE SIGNS LIST

1 light-excluding conductive electrode film layer

3 transparent conductive film

5 narrow frame touch input sheet

7 base sheet

10 fine wiring circuit pattern

12 mask

14 exposing light beam

16 first resist layer

18 second resist layer

20 capacitive touch sensor

22 outer edge portion of the narrow frame touch input sheet 5

24 central window portion of the narrow frame touch input sheet

28 external circuit

30 transparent protection film

46, 47 rhombus electrode

469, 479 connection wiring

1. A narrow frame touch input sheet comprising: one or more transparentbase sheets stacked into a layer; transparent conductive films formed ona front surface and a rear surface of the one transparent base sheet oron uppermost and lowermost surfaces of the stacked transparent basesheets; a light-excluding conductive electrode film formed on each ofthe transparent conductive films; and a first resist layer formed oneach of the light-excluding conductive electrode films, wherein thetransparent conductive films and the light-excluding conductiveelectrode films in a central window portion of the one or more basesheets are formed in desired patterns stacked without misalignmentthrough etching, after exposure and development of the first resistlayers, the transparent conductive films and the light-excludingconductive electrode films in an outer edge portion of the one or morebase sheets are formed in a fine wiring circuit pattern stacked withoutmisalignment through etching, after exposure and development of thefirst resist layers, and a circuit pattern is constituted of thetransparent conductive films in the central window portion throughremoving the first resist layers, and further etching and removing thelight-excluding conductive electrode films in the central windowportion.
 2. The narrow frame touch input sheet according to claim 1,further comprising second resist layers each of which covers thetransparent conductive film and the light-excluding conductive electrodefilm in the outer edge portion.
 3. The narrow frame touch input sheetaccording to claim 1, wherein the one or more base sheets are plasticfilms.
 4. The narrow frame touch input sheet according to claim 1,wherein the light-excluding conductive electrode film is a copper foilhaving a thickness of 20 to 1000 nm.
 5. The narrow frame touch inputsheet according to claim 1, which is a capacitive type. 6-11. (canceled)12. A method for manufacturing a narrow frame touch input sheet,comprising: forming and stacking transparent conductive films,light-excluding conductive electrode films, and first resist layerssequentially on both surfaces of a transparent base sheet; exposing anddeveloping the first resist layers simultaneously on the both surfaces;etching the transparent conductive films and the light-excludingconductive electrode films simultaneously on the both surfaces;stripping the first resist layers so as to form a fine wiring circuitpattern with the stacked transparent conductive film and light-excludingconductive electrode film in an outer edge portion on each of the twosurfaces of the base sheet; forming a second resist layer to cover thefine wiring circuit pattern on each surface of the base sheet; andetching only the light-excluding electrode conductive film layer onwhich the second resist layer is not formed, so that a circuit patternof the transparent conductive film is exposed in a central windowportion on each surface of the base sheet.
 13. A method formanufacturing a narrow frame touch input sheet comprising: forming andstacking a transparent conductive film, a light-excluding conductiveelectrode film, and a first resist layer sequentially on each of twotransparent base sheets; stacking the base sheets to be opposite to eachother so that the transparent conductive films, the light-excludingconductive electrode films, and the first resist layers are formed onboth surfaces of the stacked base sheets; exposing and developing thefirst resist layers simultaneously on the both surfaces; etching thetransparent conductive films and the light-excluding conductiveelectrode films simultaneously on the both surfaces; stripping the firstresist layers so as to form a fine wiring circuit pattern with thesequentially stacked transparent conductive film and light-excludingconductive electrode film in an outer edge portion on each of the twosurfaces of the stacked base sheets; forming a second resist layer tocover the fine wiring circuit pattern on each surface of the stackedbase sheets; and etching only the light-excluding conductive electrodefilm layer in a central window portion on which the second resist layeris not formed on each surface of the stacked base sheets, so that acircuit pattern of the transparent conductive film is exposed.
 14. Thenarrow frame touch input sheet according to claim 2, wherein the one ormore base sheets are plastic films.
 15. The narrow frame touch inputsheet according to claim 2, wherein the light-excluding conductiveelectrode film is a copper foil having a thickness of 20 to 1000 nm. 16.The narrow frame touch input sheet according to claim 3, wherein thelight-excluding conductive electrode film is a copper foil having athickness of 20 to 1000 nm.
 17. The narrow frame touch input sheetaccording to claim 14, wherein the light-excluding conductive electrodefilm is a copper foil having a thickness of 20 to 1000 nm.
 18. Thenarrow frame touch input sheet according to claim 2, which is acapacitive type.
 19. The narrow frame touch input sheet according toclaim 3, which is a capacitive type.
 20. The narrow frame touch inputsheet according to claim 4, which is a capacitive type.
 21. The narrowframe touch input sheet according to claim 14, which is a capacitivetype.
 22. The narrow frame touch input sheet according to claim 15,which is a capacitive type.
 23. The narrow frame touch input sheetaccording to claim 16, which is a capacitive type.
 24. The narrow frametouch input sheet according to claim 17, which is a capacitive type.